Oxi Hóa Anốt Hợp Kim Nhôm Ở Điện Áp Cao Trong Dung Dịch Muối Kiềm

Oxi Hóa Anốt Hợp Kim Nhôm Ở Điện Áp Cao Trong Dung Dịch Muối Kiềm

TS.Nguyễn Xuân Hoàn

Trường Đại học Công Nghiệp TP Hồ Chí Minh

SUMMARY
In order to compare the effects of  oxygen acid salt in electrolytes on the film thickness and the oxi-dation time in the process of  high voltage anodic oxidation of  aluminum alloy 6063, the oxidation films were prepared by anodic oxidation of  the aluminum alloy in the three electrolyte systems of Na2SiO3, Na2HPO4,  NaAlO2. The film thickness was determined by TT230 eddy current thickness gauge. The corrosion resist-ance of  Na2SiO3 system was evaluated through dropping corrosion testing. The surf ace morphology of  ox-idation film was observed by the scanning electronic microscope (SEM). The results show that the thickness and corrosion resistance of  the film can be significantly increased after tungstate was added in the three electrolytes. Oxidation time was extended and the hardness of  the film was increased af ter adding sodium exametaphosphate in the three electrolytes. When two additives of  tungstate and sodium hexametaphosphate
was simultaneously added in silicate nm electrolyte according to the proportion of  1:1, compact film with high corrosion resistance was formed.
Keyword: High-voltage, Alkaline salt, anodic oxidation, electrolytes, corrosion resistance.

I. Đặt vấn đề

Trong nghiên cứu này chúng tôi thực hiện với điện áp trong phạm vi từ 180V – 380V,  bởi quá trình oxi hóa sinh ra một lượng lớn tia lửa ở anốt (anodic spark deposition). Qúa trình oxi hóa anốt hợp kim nhôm thường được thực hiện tương đối nghiêm ngặt như: thời gian thực hiện từ 30 – 60 phút, nhiệt độ tương đối cao, sau khi kết thúc quá trình oxi hóa phải tiến hành bịt kín các lỗ nhỏ trên lớp phủ.